物性表物性糾錯(cuò)物性性能測(cè)試條件測(cè)試方法測(cè)試結(jié)果單位密度ASTM D792/ISO 11831.42熔融指數(shù)（流動(dòng)系數(shù)）ASTM D1238/ISO 113339g/10min吸水率 23℃/24HASTM D570/ISO 620.2%物理性能測(cè)試條件測(cè)試方法測(cè)試結(jié)果單位吸水率ASTM D5700.2%縮模率-，平行方向1.7-2.1%-，垂直方向1.7-2.1%機(jī)械性能測(cè)試條件測(cè)試方法測(cè)試結(jié)果單位拉伸強(qiáng)度ASTM D63870Mpa延伸率ASTM D63830%彎曲強(qiáng)度ASTM D790108Mpa彎曲模量ASTM D7903040MpaIZOD缺口沖擊強(qiáng)度ASTM D25649J/m洛氏硬度ASTM D78594MASTM D785120R磨耗ASTM D104413拉伸強(qiáng)度ASTM D638/ISO 52770kg/cm2(MPa)[Lb/in2]洛氏硬度ASTM D78594彎曲模量ASTM D790/ISO 1783040kg/cm2(MPa)[Lb/in2]彎曲強(qiáng)度ASTM D790/ISO 178108kg/cm2(MPa)[Lb/in2]熱性能測(cè)試條件測(cè)試方法測(cè)試結(jié)果單位燃燒性（率）UL94HB熱變形溫度ASTM D648/ISO 75136℃（℉）熔融指數(shù)ASTM D123839g/10min線膨脹系數(shù)10熱變形溫度-，1.82MPaASTM D648136°C-，0.45MPaASTM D648172°C阻燃性UL94HB